CG-Si50 is a mixture of CG-Si69 and carbon black. It has the same function as CG-Si69 and at the same time it is more convenient to operate. It works as the rubber, tire aids to improve the physical and mechanical properties. Tensile strength, tear strength, abrasion resistance and etc. can be significantly improved. Permanent deformation can be reduced, and meanwhile it can reduce the compound viscosity and improve processing performance. It is suitable for polymers like natural rubber (NR), isoprene rubber (IR), styrene-butadiene rubber (SBR), butadiene rubber (BR), nitrile rubber (NBR), ethylene-propylene-diene rubber (EPDM), etc.

KH-560 is a kind of coupling agent with epoxy group. It can be used as caulking glue or sealant of polysulfide and polyurethane, adhesive of epoxy resin, and also can be used in thermosetting resin of filling or reinforcement mode, glass fiber adhesive and thermoplastic resin of inorganic filler or glass reinforcement, etc. Improve intensity properties of hard composite materials which use glass fiber roving as reinforcement. Keep intensity at maximum point after humidity period. Enhance electrical properties of epoxy resin-based sealants, packaging materials, and printed circuit boards. It is the result of improving the adhesiveness between fillers or between resin and matrix. Enhance electrical properties of composite materials of inorganic filling, including nylon and polybutylene terephthalate. Be effiective to various fillers, matrix, clay, talc, aedelforsite, silica and quartz, or metals like aluminum, cooper and iron. Improve cohesiveness of caulking glue and sealant, with water containing acrylic latex, used in polyurethane and epoxy resin coatings. It can improve the solubility, dispersity and fluidity of adhesive when put it into the organic toner.

CG-Si69 is a kind of silane coupling agent with multiple functional groups successfully used in rubber industry to improve modulus and tensile strength of rubber, to reduce the compound viscosity and save process energy consumption. It is especially applicable for polymers with double bond or rubber formulation with hydroxyl fillers. The suitable fillers include silica, silicate, clay, etc. The suitable rubber include natural rubber (NR), Butadiene styrene rubber (SBR), Isoprene rubber (IR), Butadiene rubber (BR),Acrylonitrile butadiene rubber (NBR), Ethylene propylene diene rubber (EPDM), etc.